The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) Després de l'ajust d'alta temperatura i el tractament criogènic, la solució s'escalfa primer a 950 graus durant 90 minuts. A causa de l'augment del punt Ms, es pot obtenir una petita quantitat de martensita refredant-se a temperatura ambient; quantitat de martensita.
(3) Després del tractament de la solució mitjançant el mètode de deformació en fred, la deformació en fred es realitza a temperatura ambient. La quantitat de martensita formada a la canonada sense soldadura 904L durant la deformació en fred està relacionada amb la quantitat de deformació i la composició de la canonada d'acer inoxidable 904L.
Els tres mètodes anteriors són mètodes utilitzats habitualment per al tractament de la solució de canonades d'acer inoxidable. Espero que et puguin ajudar.